- Material: Polyolefin
- Shrinkage: 2:1 Sleeves for bus bar 6÷24 KV – 36 KV
- Scope: Electrical and mechanical bus bar insulation up to 24KV
- Minimum shrinkage temperature: +100 °C
- Min/max operating temperature: -55°C to +105°C
- Color: Brick red
- Shrinkage ratio: 30%
- Flexibility: excellent
- self-extinguishing: self-extinguishing in 60 seconds according to ASTMD2671
- Water absorption: < 0.5% according to ISO52 Standard (336 hours at 23°C)
- Tensile strength: ≥ 11.8 MPA according to ASTMD2671
- Tensile strength after aging: ≥ 10 MPA (168 hours at 120°C)
- Elongation: ≥ 550%
- Elongation after aging: ≥ 450% (168 hours at 120°C)
- Dielectric strength: ≥ 20 KV/mm
- Volume resistivity: ≥ 10 13 Ω.cm according to IEC93 Standard
- Constant volume: 3.5 (max.) according to IEC250
- Copper corrosion: none (168 hours at 120°C)
NTMT24KV BUS BAR 24KV Heat shrink sleeve with internal adhesive
The NTMT24KV Series heat shrink sleeve is made of polyolefin. The inner part of the sleeve is coated with a hot-melt adhesive which, during the shrinking phase, melts around the object in order to guarantee the best fixing and protection from water and moisture infiltration. It is usually used to electrically and mechanically isolate bus bars up to 24KV and irregularly shaped objects, where it is not possible to mount a closed sleeve.
- 2:1 shrinkage ratio. The sleeve shrinks 2 times with respect to the initial diameter. Sleeves for bus-bar 6÷24 KV – 36 KV
- Available diameters: from 25.0mm to 100.0mm
- Operating temperature from -55°C to +105°C
- Conforms to ASTMD2671, ISO52, IEC243, IEC93, IEC250
download the technical data sheet